NUI KULA KULA KULA
321 kila kila 6*1mm wili paipu
| Kūlana | ʻO ASTM A213 (Papa Awelika) a me ASTM A269 |
| ʻO ka ʻili ʻili ʻili ʻili ma waho ke anawaena | 1/16" a hiki i 3/4" |
| ʻO ka mānoanoa o ka paipu huila kuhiliʻole | .010″ ma o .083” |
| Nā Papa Hoʻopaʻa ʻAi ʻAi ʻAi Kuhili ʻole | SS 201, SS 202, SS 304, SS 304L, SS 309, SS 310, SS 316, SS 316L, SS 317L, SS 321, SS 347, SS 904L |
| Nui Rnage | 5/16, 3/4, 3/8, 1-1/2, 1/8, 5/8, 1/4, 7/8, 1/2, 1, 3/16 iniha |
| ʻoʻoleʻa | Micro a me Rockwell |
| Hoʻomanawanui | D4/T4 |
| Ka ikaika | Puka a me ka Tensile |
NA PAPA KUHIKUHI O NA PAPA PALAPALA STEEL
321 kila kila 6*1mm wili paipu
| KANAWAI | WERKSTOFF NR. | UNS | JIS | BS | GOST | AFNOR | EN |
|---|---|---|---|---|---|---|---|
| SS 304 | 1.4301 | S30400 | SUS 304 | 304S31 | 08Х18Н10 | Z7CN18-09 | X5CrNi18-10 |
| SS 304L | 1.4306 / 1.4307 | S30403 | SUS 304L | 3304S11 | 03Х18Н11 | Z3CN18-10 | X2CrNi18-9 / X2CrNi19-11 |
| SS 310 | 1.4841 | S31000 | SUS 310 | 310S24 | 20Ch25N20S2 | – | X15CrNi25-20 |
| SS 316 | 1.4401 / 1.4436 | S31600 | SUS 316 | 316S31 / 316S33 | – | Z7CND17-11-02 | X5CrNiMo17-12-2 / X3CrNiMo17-13-3 |
| SS 316L | 1.4404 / 1.4435 | S31603 | SUS 316L | 316S11 / 316S13 | 03Ch17N14M3 / 03Ch17N14M2 | Z3CND17-11-02 / Z3CND18-14-03 | X2CrNiMo17-12-2 / X2CrNiMo18-14-3 |
| SS 317L | 1.4438 | S31703 | SUS 317L | – | – | – | X2CrNiMo18-15-4 |
| SS 321 | 1.4541 | S32100 | SUS 321 | – | – | – | X6CrNiTi18-10 |
| SS 347 | 1.4550 | S34700 | SUS 347 | – | 08Ch18N12B | – | X6CrNiNb18-10 |
| SS 904L | 1.4539 | N08904 | SUS 904L | 904S13 | STS 317J5L | Z2 NCDU 25-20 | X1NiCrMoCu25-20-5 |
SS COIL TUBE KEMIKAL COMPOSITION
321 kila kila 6*1mm wili paipu
| Papa | C | Mn | Si | P | S | Cr | Mo | Ni | N | Ti | Fe | |
|---|---|---|---|---|---|---|---|---|---|---|---|---|
| SS 304 Coil Paipu | min. | 18.0 | 8.0 | |||||||||
| max. | 0.08 | 2.0 | 0.75 | 0.045 | 0.030 | 20.0 | 10.5 | 0.10 | ||||
| SS 304L Paipu Coil | min. | 18.0 | 8.0 | |||||||||
| max. | 0.030 | 2.0 | 0.75 | 0.045 | 0.030 | 20.0 | 12.0 | 0.10 | ||||
| SS 310 Coil Paipu | 0.015 ka nui | 2 max | 0.015 ka nui | 0.020 ka nui | 0.015 ka nui | 24.00 26.00 | 0.10 ka nui | 19.00 21.00 | 54.7 min | |||
| SS 316 Coil Paipu | min. | 16.0 | 2.03.0 | 10.0 | ||||||||
| max. | 0.035 | 2.0 | 0.75 | 0.045 | 0.030 | 18.0 | 14.0 | |||||
| SS 316L Coil Paipu | min. | 16.0 | 2.03.0 | 10.0 | ||||||||
| max. | 0.035 | 2.0 | 0.75 | 0.045 | 0.030 | 18.0 | 14.0 | |||||
| SS 317L Paipu Coil | 0.035 ka nui | 2.0 ka nui | 1.0 ka nui | 0.045 ka nui | 0.030 ka nui | 18.00 20.00 | 3.00 4.00 | 11.00 15.00 | 57.89 min | |||
| SS 321 Paipu Coil | 0.08 ka nui | 2.0 ka nui | 1.0 ka nui | 0.045 ka nui | 0.030 ka nui | 17.00 19.00 | 9.00 12.00 | 0.10 ka nui | 5(C+N) 0.70 ka nui | |||
| SS 347 Paipu Coil | 0.08 ka nui | 2.0 ka nui | 1.0 ka nui | 0.045 ka nui | 0.030 ka nui | 17.00 20.00 | 9.0013.00 | |||||
| SS 904L Coil Paipu | min. | 19.0 | 4.00 | 23.00 | 0.10 | |||||||
| max. | 0.20 | 2.00 | 1.00 | 0.045 | 0.035 | 23.0 | 5.00 | 28.00 | 0.25 | |||
NA WAIWAI MECHANICAL COIL STEEL STEEL
321 kila kila 6*1mm wili paipu
| Papa | ʻO ka mānoanoa | Lae hehee | Ikaika U'i | Ka ikaika o ka hua (0.2%offset) | ʻO ka lōʻihi |
|---|---|---|---|---|---|
| SS 304/ 304L Paipu Coil | 8.0 g/cm3 | 1400 °C (2550 °F) | Psi 75000, MPa 515 | Psi 30000, MPa 205 | 35 % |
| SS 310 Coil Paipu | 7.9 g/cm3 | 1402 °C (2555 °F) | Psi 75000, MPa 515 | Psi 30000, MPa 205 | 40 % |
| SS 306 Paipu Coil | 8.0 g/cm3 | 1400 °C (2550 °F) | Psi 75000, MPa 515 | Psi 30000, MPa 205 | 35 % |
| SS 316L Paipu Coil | 8.0 g/cm3 | 1399 °C (2550 °F) | Psi 75000, MPa 515 | Psi 30000, MPa 205 | 35 % |
| SS 321 Paipu Coil | 8.0 g/cm3 | 1457 °C (2650 °F) | Psi 75000, MPa 515 | Psi 30000, MPa 205 | 35 % |
| SS 347 Paipu Coil | 8.0 g/cm3 | 1454 °C (2650 °F) | Psi 75000, MPa 515 | Psi 30000, MPa 205 | 35 % |
| SS 904L Paipu Coil | 7.95 g/cm3 | 1350 °C (2460 °F) | Psi 71000, MPa 490 | Psi 32000, MPa 220 | 35 % |
Ka manawa hoʻouna: Mei-08-2023